Maha Cement – OPC 53 grade

Maha Cement – OPC 53 grade cement, is a high strength, best quality cement designed to suit the modern construction practices. It is manufactured with excellent quality clinker, containing high percentage (56-60%) of Tri-calcium Silicate (C3S), and optimum quantity of gypsum. This cement is ideal for designing high strength, high performance concrete used in high rise buildings, bridges, flyovers, pre-stressed concrete applications, under water concreting, concrete roads etc. Due to its uniform and consistent 28 days’ compressive strength 60 MPa. It is the most preferred brand by Ready Mix Concrete manufacturers and infrastructure project engineers.

Please refer the table below for its typical values as against requirement as per IS 269-2015

Physical Requirements

Requirement as per IS 269 : 2015

Maha Cement OPC 53

Fineness

Specific Surface (m2/kg)

225 (min)

295

Setting Time

a. Initial (minutes)

b. Final (minutes)

30 (min)

600 (max)

165

240

Soundness

Expansion of unaerated cement

a. By LeChatelier Method (mm)

b. By Auto Clave (%

-

10 (max)

0.8 (max)

-

1.0

0.074

Compressive Strength

a. 72 ± 1 hr i.e. 3 days (M Pa)

b. 168 ± 2 hr i.e. 7 days (M Pa)

c. 672 ± 4 hr i.e. 28 days (M Pa)

27 (min)

37 (min)

53 (min)

38

48

60

Benefits of Maha Cement – OPC 53 grade

Maha Cement - Strength

Good Compressive
Strength

Maha Cement - Analytic Reports

satisfactory durability characteristics

Maha Cement - Maha Cement Bag
Maha Cement - Analytic Reports

higher grade
cements

Maha Cement - Work

Suitability for General Construction